PET films are produced under manufacturer’s TU and used for food packing and as a basis of multilayer packing materials for printing, lamination and metallization. The films highly resist gas, moisture, foreign smells penetration, thus securing longer keeping of the packed product. The film is highly resistant to punctures, it has high mechanical strength, transparence and moisture resistance, and it stands the temperatures from -70 °С up to +150 °С. We can offer transparent corona or chemically treated PET film. We can cut the film to the width required by the customer.
See technical characteristics of corona treated film.
| # |
Item |
Test Method |
Values |
| 1 |
Physical |
| 1.1 |
Thickness, mic |
|
ASTM D 1505 |
12 |
15 |
19 (20) |
25 (23) |
35 (36) |
50 |
| 1.2 |
Specific weight, m²/kg |
|
ASTM D 1505 |
59.5 |
47.6 |
37.6 |
28.6 |
|
14.3 |
| 1.3 |
Square meter weight, g/m² |
|
ASTM D 1505 |
16.8 |
21 |
26.6 |
35 |
|
70 |
| 1.4 |
Elasticity modulus, not less, N/mm² |
MD |
ASTM D 882 |
4000 |
3000 |
| TD |
4200 |
3500 |
| 1.5 |
Tensile strength at yield, not less, N/mm² |
MD |
ASTM D 882 |
210 |
190 |
175 |
| TD |
210 |
200 |
| 1.6 |
Elongation at break, not less, % |
MD |
ASTM D 882 |
140 |
150 |
| TD |
130 |
140 |
| 1.7 |
Surface tension, not less, dyne/cm |
Not treated |
ASTM D 2578 |
42 |
| Chemically treated |
54 |
| 1.8 |
Kinetic coefficient of friction |
Not treated |
ASTM D 1894 E |
0.5 |
| 2 |
Optic |
| 2.1 |
Haze, % |
|
ASTM D 1003 |
3 |
4 |
5 |
5.5 |
| 2.2 |
Gloss, % |
|
ASTM D 2457 |
85 |
| 3 |
Thermal |
| 3.1 |
Shrinkage at 150°C / 20', % |
MD |
ASTM D 1204 |
2 |
| TD |
0.4 |
0.5 |
| 4 |
Barrier |
| 4.1 |
Water vapour penetration MVTR, g/m²/24 h |
|
ASTM F 1249 27°C-65% RH |
30 |
28 |
22 |
15 |
10 |
| 4.2 |
Oxygen penetration, cm³/m²/24 h. atm |
|
ASTM D 3985 |
100 |
75 |
70 |
50 |
40 |
MD - machine direction,
TD - transverse direction.
See technical characteristics of chemically treated film.
| # |
Item |
Test Method |
Values |
| 1 |
Physical |
| 1.1 |
Thickness, mic |
|
ASTM D 1505
| 12 |
15 |
19 (20) |
25 |
30 |
| 1.2 |
Specific weight, m²/kg |
|
ASTM D 1505 |
59.5 |
47.6 |
37.6 |
28.6 |
23.8 |
| 1.3 |
Square meter weight, g/m² |
|
ASTM D 1505 |
16.8 |
21 |
26.6 |
35 |
42 |
| 1.4 |
Elasticity modulus, not less, N/mm² |
MD |
ASTM D 882 |
4000 |
| TD |
4200 |
| 1.5 |
Tensile strength at yield, not less, N/mm² |
MD |
ASTM D 882 |
210 |
| TD |
210 |
| 1.6 |
Elongation at break, not less, % |
MD |
ASTM D 882 |
140 |
150 |
| TD |
130 |
140 |
| 1.7 |
Surface tension, not less, dyne/cm |
Not treated |
ASTM D 2578 |
42 |
| Chemically treated |
58 |
| 1.8 |
Kinetic coefficient of friction |
Not treated |
ASTM D 1894 E |
0.5 |
| 2 |
Optic |
| 2.1 |
Haze, % |
|
ASTM D 1003 |
3 |
4 |
| 2.2 |
Gloss, % |
|
ASTM D 2457 |
85 |
| 3 |
Thermal |
| 3.1 |
Shrinkage at 150°C / 20', % |
MD |
ASTM D 1204 |
2 |
| TD |
0.4 |
| 4 |
Barrier |
| 4.1 |
Water vapour penetration MVTR, g/m²/24 h |
|
ASTM F 1249 27°C-65% RH |
30 |
28 |
25 |
|
| 4.2 |
Oxygen penetration, cm³/m²/24 h. atm |
|
ASTM D 3985 |
100 |
75 |
50 |
|
MD - machine direction,
TD - transverse direction.
Tel./fax: +7 (4922) 33-82-06 and 33-65-71
E-mail: This email address is being protected from spambots. You need JavaScript enabled to view it.
Head of Packaging Department
Anna V. Kovalyeva
+7 (919) 011-43-96 and (930) 749-11-14
E-mail: This email address is being protected from spambots. You need JavaScript enabled to view it.
Skype: ksk-kovaleva
Manager of Packaging Department
Anton A. Trushkin
+7 (915) 767-17-06 and (930) 031-71-48
E-mail: This email address is being protected from spambots. You need JavaScript enabled to view it.
Skype: ksk-trushkin
Manager of Packaging Department
Vasily V. Kazakov
+7 (910) 182-13-50 and (920) 937-60-25